Brominated Epoxy Vinyl Ester Resins

VE resins are a combination of both polyester resin and epoxy resins best properties. While they have high mechanical strength values similar to epoxy resins, they are easy to apply similar to unsaturated polyester resins.

Flame retardant, halogenated vinyl ester resins, provides flame retardancy and chemical resistance, solvent resistance. They are suitable for applications requiring mechanical strength. Suitable for hand lay-up, infusion, RTM production methods.

Döküm Tipi Vinyl ester resins have low polar groups on chemical backbone and are more resistant to hydrolysis compared to polyester resins.
  • Chemical Resistance Guide
  • Refer to our Chemical Resistance Guide for more information about use of resins in different chemical environments.
SONRAKİ ÖNCEKİ
  •  
  • Product Description
  • Technical Data Sheets
  • Safety Data Sheets
  • Chemical Structure
  • Available Modifications
  • Viscosity
  • Thixotropy
  • Monomer Content
  • Acid Value [mg KOH/g]
  • Gel Time
  • Tensile Strength
  • Elongation at Break,Tensile
  • Flexural Strength
  • HDT [0,45 MPa]
  • Barcol Hardness, 934
  • Volumetric Shrinkage
  • Remarks
  • Highlights
  • Primary Usages
  • Polives 710
  • RTM / Infusion type flame retardant vinyl ester
  • PDF
  • PDF
  • VE
  • 400-500
  • N/A
  • 34-38
  • max. 10
  • 20-30
  • 75
  • 3
  • 165
  • 110
  • 35
  • 7,7
  • OT1 , OT5
  • - Increased flame retardancy with antimony
    - High hydrolytic and chemical resistance
    - Excellent fiber wet-out
  • Chemical resistant, flame retardant applications such as boiler units, engine insulation, pipelines and chemical storage tanks and yachts.
  • Polives 710-I
  • RTM / Infusion type flame retardant vinyl ester resin
  • PDF
  • PDF
  • VE
  • 200-250
  • N/A
  • 36-39
  • max. 10
  • 30-35
  • 70
  • 3
  • 165
  • 105
  • 35
  • 7,7
  • OT1 , OT5
  • - High chemical resistance against various chemicals, acids, alkalis.
    - High corrosion resistance
    - Perfect mechanical properties and impact resistance
    - Very good fiber wetting
    - Flame retardancyLow viscosity
  • Chemical resistant, flame retardant applications such as boiler units, engine insulation, pipelines and chemical storage tanks and yachts.
  • Polives 710-TA
  • Flame retardant thixotropic high performance vinyl ester resin
  • PDF
  • PDF
  • VE
  • 200-250
  • N/A
  • 36-39
  • max. 10
  • 30-35
  • 70
  • 6.5
  • 165
  • 105
  • 35
  • 7,7
  • OT1 , OT5
  • - High chemical resistance against various chemicals, acids, alkalis, solvents.
    - High corrosion resistance
    - Excellent mechanical properties and impact resistance
    - Very good fiber wetting
    - Flame retardancy
    - Thixotropic, no sagging on vertical surfaces
    - Pre-accelerated, contains cobalt
  • Chemical resistant, flame retardant applications such as boiler units, engine insulation, pipelines and chemical storage tanks and yachts.
  • Polives 710-TA-LSE
  • Flame retardant LSE high performance vinyl ester resin
  • PDF
  • PDF
  • VE
  • -
  • N/A
  • -
  • max. 10
  • -
  • 70
  • 7
  • 165
  • 105
  • 35
  • 7,7
  • OT1 , OT5
  • - High chemical resistance against various chemicals, acids, alkalis, solvents.
    - High corrosion resistance
    - Excellent mechanical properties and impact resistance
    - Very good fiber wettingFlame retardancy
    - Thixotropic, contains styrene emission suppressants (LSE)
    - Pre-accelerated, contains cobalt
  • Chemical resistant, flame retardant applications such as boiler units, engine insulation, pipelines and chemical storage tanks and yachts.

Modification Description

  • FR   Filled flame retardant
  • D*   Filled (*with filler content)
  • T Thixotropic (no sagging)
  • A Cobalt preaccelerated
  • ABP Amine preaccelerated
  • UV UV Curing
  • L   UV light stabilized
  •   I Lower viscosity
  •   V Higher viscosity
  •   LSE   LSE (low styrene emission)
  •   H* Gel time customized (at room temperature) * minutes
  • H40 Optimized for summer season. Gel time (at room temperature) 40 minutes.
  • H20 Optimized for winter season. Gel time (at room temperature) 20 minutes.
  •   COLOR   White or custom color options

Gelcoat Customizations
Polijel gelcoat table descriptions and modifications.

  • Spray Application (airless preferred)
  • Brush or Roller Application
  • Color Option: White colored
  • Color Option: Light colored (pastel)
  • Color Option: PRO colored

Production Quantity Depending on Process (parts/year)
Regardless of product dimension and complexity..

İlk sen haberdar ol!
Poliya’nın güncel haberlerinden ve yeni ürünlerinden haberdar olmak ister misiniz?
İzin ver Daha Sonra
x

Haberlerden Geri Kalmayın

En son haberlerimizden ve ürünlerimizden ilk haberdar olmak için lüten aşağıdaki alanları doldurunuz..