ZERO RTM System
Polipol 3387-ZERO is a zero shrink resin which is specially designed for RTM productions. It provides exceptional dimensional stability and excellent surface quality. When Polipol 3387- ZERO is used as RTM resin in molds produced with Polipol 321-ZERO tooling resin, it is possible to obtain a high degree of dimensional conformity to model and design.
ZERO RTM System Components
① ZERO Tooling Resin (for mold making)
② Gelcoat - Polijel 210, 212, 213 or 215 (depends on performance needed)
③ RTM Resin - Polipol 3387-ZERO
ZERO Tooling System Components
① Tooling Gelcoat - Polijel P-272 or P-220 (depends on performance needed)
② Barrier Coat - Polijel BC-782
③ Skin Coat - Polives 701-TA
④ Tooling Resin - Polipol 321-ZERO
- Chemical Resistance Guide
Refer to our Chemical Resistance Guide for more information about use of resins in different chemical environments.
| Test | Method | Polipol 3387 ZERO | Lamination of 4 layers of Chopped Strand Mat 450gr/m2 |
||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Flexural Strength (MPa) | ISO 0178 | 120 | 270 | ||||||||||
| Modulus of Elasticity, Flexural (MPa) | ISO 0178 | 3700 | 8300 | ||||||||||
| Elongation at Break, Flexural (%) | ISO 0178 | 3.5 | 5.8 | ||||||||||
| Tensile Strength (MPa) | ISO 0527 | 62 | 140 | ||||||||||
| Modulus of Elasticity, Tensile (MPa) | ISO 0527 | 2950 | 6800 | ||||||||||
| Elongation at Break, Tensile (%) | ISO 0527 | 2.4 | 3.8 | ||||||||||
| Izod Impact Strenght (kj/m2) | ISO 0180 | 8 | 13 | ||||||||||
| HDT [0,45 MPa] (°C) | ISO 0075-B | 115 | - | ||||||||||
| Glass Transition Temperature (°C) | ASTM-E 1640-04 | 127 | - | ||||||||||
| Water Absorption (%) | ISO 0062 | 0.17 | - | ||||||||||
| Barcol Hardness, 934 (Barkol) | ASTM-D 2583 | 44 | - | ||||||||||
| Lineer Shrink (%) | ASTM-C 356 | 0.05 | - | ||||||||||
Packing Types
You can choose any package type suitable for your production system or you can get further information from our sales department regarding container options.
-
25.000 kg
ISO Tank Container Optional Steam heating line Optional Long term renting -
18 Kg
Pail -
20 Kg
Bucket -
230 Kg
Barrel -
230 Kg
Recond. Barrel -
1.100 Kg
IBC -
1.100 Kg
Recond. IBC
Modification Description
- FR Filled flame retardant
- D* Filled (*with filler content)
- T
Thixotropic (no sagging) - A
Cobalt preaccelerated - ABP Amine preaccelerated
- UV UV Curing
- L UV light stabilized
- I
Lower viscosity - V Higher viscosity
- LSE LSE (low styrene emission)
- H*
Gel time customized (at room temperature) * minutes 
H40 Optimized for summer season. Gel time (at room temperature) 40 minutes.
H20 Optimized for winter season. Gel time (at room temperature) 20 minutes.- COLOR White or custom color options
Gelcoat Customizations
Polijel gelcoat table descriptions and modifications.
Spray Application (airless preferred)
Brush or Roller Application
Color Option: White colored
Color Option: Light colored (pastel)
Color Option: PRO colored
Production Quantity Depending on Process (parts/year)
Regardless of product dimension and complexity..